17-4 Precipitation Hardening also known as Type 630 is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and a moderate level of corrosion resistance.
17-4 PH Stainless Steel supplied in Sheet and Plate - AMS
17-4 PH is a martensitic, chromium-nickel-copper precipitation-hardening stainless steel. 17-4 PH stainless steel is capable of attaining a wide range of strength and toughness properties depending on the precipitation or aging temperature used in hardening. Its valuable combination of high strength, good corrosion resistance and toughness in both base metals and welds gives designers
17-4 stainless is an age-hardening martensitic stainless combining high strength with the corrosion resistance of stainless steel. Hardening is achieved by a short-time, simple low-temperature treatment. Unlike conventional martensitic stainless steels, such as type 410, 17-4 is quite weldable.
IN METAL AM Testing and Analysis of Aerospace Parts Made by Additive Manufacturing Chemistry –ICP/Gas PSD Density Metal AM Build Heat Treat/HIP Mechanical Testing Stress Relief EDM Morphology and Size (174PH), Poor Flow and Poor Internal …
Competitive Price For Alloy 630 Plate Stainless Steel 17
17-4PH stainless steel products are widely used in petroleum chemistry, electric power, machinery manufacturing, automobile manufacturing, aerospace, offshore drilling, military and other industrial fields.
17/4 PH (630) U.S. ALLOY CO. - Washington Alloy Co.
17/4 PH (630) Welding Wire and Rod U.S. ALLOY CO. dba Washington Alloy 7010-G Reames Rd. Charlotte, NC 28216 weldingwire WASHINGTON ALLOY’S Quality Management System is Certified to ISO 9001:2008 Cert # 05-R0925 Washington Alloy Company believes that all information and data given is correct. Use this information to assist in making your
AK Steel 17-4 PH® Precipitation Hardening Stainless Steel
Metal; Ferrous Metal; Martensitic; Stainless Steel; Precipitation Hardening Stainless. Material Notes: AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds.
17-4 PH has good fabricating characteristics and can be age hardened by a single step, low temperature treatment. 17-4 PH is a versatile material widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.
AISI 4340 steel is a medium carbon, low alloy steel known for its toughness and strength in relatively large sections. AISI 4340 is also one kind of nickel chromium molybdenum steels. 4340 alloy steel is generally supplied hardened and tempered in the tensile range of 930 – 1080 Mpa.
Chemical and electrochemical etching of stainless steel
2001. A. One of many chemicals to etch stainless steel is ferric chloride solution => It can be brought as a solution or made from solid, if you make from solid take care as it generates a fair amount of heat on dissolution, about 30% by weight is a good enough etch.
The chemistry of the material met the requirements of the applicable specifications, as shown in Table 3. C. Heat Treatment The bar stock of both alloys was received in the solution annealed condition (Condition A). Standard R.R. Moore rotating beaun fatigue specimens were rouqh